Avaliação do comportamento de revestimento de argamassa submetido a envelhecimento acelerado e à carbonatação

Show simple item record

metadataTrad.dc.contributor.author Menegotto, Camila Werner;
metadataTrad.dc.contributor.authorLattes http://lattes.cnpq.br/2844341743262219;
metadataTrad.dc.contributor.advisor Kazmierczak, Claudio de Souza;
metadataTrad.dc.contributor.advisorLattes http://lattes.cnpq.br/8647433523617676;
metadataTrad.dc.publisher Universidade do Vale do Rio dos Sinos;
metadataTrad.dc.publisher.initials Unisinos;
metadataTrad.dc.publisher.country Brasil;
metadataTrad.dc.publisher.department Escola Politécnica;
metadataTrad.dc.language pt_BR;
metadataTrad.dc.title Avaliação do comportamento de revestimento de argamassa submetido a envelhecimento acelerado e à carbonatação;
metadataTrad.dc.description.resumo Os ciclos contínuos de molhagem e secagem a que revestimentos de argamassa são submetidos ao longo de sua vida, associados ao efeito da carbonatação e aos impactos provenientes do uso, ocasionam esforços de tração e cisalhamento ao revestimento que poderão causar microfissuras na estrutura do revestimento e, portanto, influenciar na forma de ruptura do material. Em consequência, é recomendado conferir um baixo módulo de elasticidade às argamassas, sendo este responsável pela capacidade destas de se deformarem sem fissurar ao receber tensões. No entanto, tal propriedade é afetada pelo processo de envelhecimento e pela carbonatação, que podem tornar a argamassa mais rígida ou mais elástica. O objetivo desta pesquisa é avaliar o efeito da carbonatação e do envelhecimento acelerado no comportamento da argamassa quando submetida a esforços de tração, ao ser aplicada sobre substratos distintos, bem como estimar o módulo de elasticidade por correlação de imagem digital (CID). Foram utilizados dois substratos cerâmicos com diferentes valores de absorção capilar e rugosidade. Foram moldadas argamassas no traço 1:1:4 (cimento:cal:areia), CP II-F 40 e cal CH-I, relação a/agl 0,80. As amostras foram curadas durante 56 dias em ambiente controlado. Foram determinados o índice de vazios, a absorção de água por capilaridade e a resistência à tração antes e após os processos de envelhecimento e carbonatação. A análise de tensões e deformações foi realizada aplicando a metodologia CID e posteriormente calculando o módulo de elasticidade com o auxílio de softwares específicos. Concluiu-se que o envelhecimento acelerado eleva a absorção de água capilar e reduz a resistência de aderência e que a carbonatação é influenciada pelo tipo de substrato ao qual a argamassa está aplicada. Os módulos de elasticidade calculados a partir de CID mostraram-se coerentes com os valores encontrados na literatura e indicaram que há diferenças de módulo ao longo da espessura do revestimento.;
metadataTrad.dc.description.abstract The continuous wetting and drying cycles to which mortar coatings are subjected throughout their life, associated with the effect of carbonation and the impacts arising from use, cause traction and shear stresses to the coating that, throughout its useful life, may cause microcracks in the structure of the coating and, therefore, influence the way the material ruptures. Consequently, it is recommended to give mortars a low modulus of elasticity, which is responsible for their ability to deform without cracking when subjected to stress. However, this property is affected by the aging process and carbonation, which can make the mortar more rigid or more elastic. The objective of this research is to evaluate the effect of carbonation and accelerated aging on the behavior of the mortar when subjected to tensile stress, when applied on different substrates, as well as to estimate the modulus of elasticity by digital image correlation (CID). Two ceramic substrates with different capillary absorption and roughness values were used. Mortars were molded in the proportion 1:1:4 (cement:lime:sand), CP II-F 40 and lime CH-I, a/gl ratio 0.80. Samples were cured for 56 days in a controlled environment. The voids index, water absorption by capillarity and tensile strength were determined before and after the aging and carbonation processes. The stress and deformation analysis was carried out applying the CID methodology and later calculating the modulus of elasticity with the aid of specific software. It was concluded that accelerated aging increases capillary water absorption and reduces bond strength and that carbonation is influenced by the type of substrate to which the mortar is applied. The modulus of elasticity calculated from the CID were coherent with the values found in the literature and indicated that there are modulus differences along the thickness of the coating.;
metadataTrad.dc.subject Argamassa de revestimento; Envelhecimento acelerado; Carbonatação; Módulo de elasticidade; Coating mortar; Accelerated aging; Carbonation; Modulus of elasticity;
metadataTrad.dc.subject.cnpq ACCNPQ::Engenharias::Engenharia Civil;
metadataTrad.dc.type Dissertação;
metadataTrad.dc.date.issued 2023-05-28;
metadataTrad.dc.description.sponsorship CAPES - Coordenação de Aperfeiçoamento de Pessoal de Nível Superior;
metadataTrad.dc.rights openAccess;
metadataTrad.dc.identifier.uri http://www.repositorio.jesuita.org.br/handle/UNISINOS/12622;
metadataTrad.dc.publisher.program Programa de Pós-Graduação em Engenharia Civil;