Influência de resíduos de rochas ornamentais nas propriedades de argamassas de revestimento

Show simple item record

metadataTrad.dc.contributor.author Melo, Rorennychollas Ferreira;
metadataTrad.dc.contributor.authorLattes http://lattes.cnpq.br/9820962930369680;
metadataTrad.dc.contributor.advisor Kazmierczak, Claudio de Souza;
metadataTrad.dc.contributor.advisorLattes http://lattes.cnpq.br/8647433523617676;
metadataTrad.dc.publisher Universidade do Vale do Rio dos Sinos;
metadataTrad.dc.publisher.initials Unisinos;
metadataTrad.dc.publisher.country Brasil;
metadataTrad.dc.publisher.department Escola Politécnica;
metadataTrad.dc.language pt_BR;
metadataTrad.dc.title Influência de resíduos de rochas ornamentais nas propriedades de argamassas de revestimento;
metadataTrad.dc.description.resumo A reutilização do resíduo de rochas ornamentais pode propiciar benefícios a matrizes cimentícias, proporcionando um melhor destino para o mesmo. O presente trabalho apresenta resultados da substituição parcial de cimento por resíduos de rochas ornamentais (lama). A substituição ocorreu em argamassas de revestimento, confeccionadas com cimento CP-V ARI, no traço 1:1:6 (cimento, cal, areia). O teor de água foi definido em função da consistência (fixada em 260±5 mm). O potencial para melhoria das propriedades da argamassa foi avaliado a partir da determinação de sua distribuição granulométrica, da superfície específica e da possibilidade do resíduo a gerar nucleação. As diferenças nas propriedades da argamassa de revestimento foram avaliadas no estado fresco, endurecido e na forma de revestimento. No estado fresco, foram determinadas as seguintes propriedades: consistência (mesa de espalhamento), retenção de água e densidade de massa. No estado endurecido, foram determinadas as seguintes propriedades: resistência à compressão e à tração, densidade de massa, variação volumétrica, módulo de elasticidade, absorção de água por imersão, índice de vazios e absorção de água por capilaridade. No revestimento, foi avaliado a resistência de aderência por tração da argamassa aplicada em bloco cerâmico. Observa-se que a substituição do cimento por resíduos de rochas ornamentais influenciou as argamassas através do efeito filer, atuando no efeito físico, melhorando o empacotamento granulométrico das argamassas substituídas. Os resultados indicam que o melhor teor de substituição foi de 15% do cimento por resíduos de rochas ornamentais. A substituição não comprometeu o desempenho das propriedades das argamassas produzidas. Desta forma, as argamassas com diferentes teores de substituição obtiveram resultados semelhantes à argamassa referência com menores teores de cimento. Os resultados obtidos indicam que os resíduos de rochas ornamentais têm bom potencial para serem utilizados como filer em matrizes cimentícias.;
metadataTrad.dc.description.abstract The reuse of ornamental rock waste can provide benefits to cementitious matrices, providing a better destination for it. The following paper studies the partial replacement of cement by residual ornamental rocks (mud). The replacement took place in coating mortars, made with CP-V ARI cement, in the 1:1:6 line (cement, lime, sand). The water content was defined according to the consistency (fixed at 260 ± 5 mm). The potential for improving the properties of the mortar was evaluated from the determination of its granulometric distribution, the specific surface and the possibility of the waste to generate nucleation. The differences in the properties of the coating mortar were evaluated in the fresh and hardened state, and in the coating form. In the fresh state, the following properties were determined: consistency (spreading table), water retention and mass density. In the hardened state, the following properties were determined: compressive and tensile strength, mass density, volumetric variation, modulus of elasticity, water absorption by immersion, void index and water absorption by capillarity. In the coating, the tensile bond strength of the mortar applied in a ceramic block was evaluated. It is observed that the replacement of cement by waste of ornamental rocks influenced the mortars through the filer effect, acting on the physical effect, improving the granulometric packaging of the replaced mortars. The results indicate that the best content of substitution was 15% of cement for ornamental rock waste. The substitution did not compromise the performance of the produced mortar properties. Thereby, mortars with different contents of substitution obtained similar results to the reference mortar with lower levels of cement. The results obtained indicate that the ornamental rock waste has good potential to be used as filer in cementitious matrices.;
metadataTrad.dc.subject Resíduos; Rochas ornamentais; Argamassa de revestimento; Desempenho; Meio ambiente; Waste; Ornamental rocks; Coating mortar; Performance; Environment;
metadataTrad.dc.subject.cnpq ACCNPQ::Engenharias::Engenharia Civil;
metadataTrad.dc.type Dissertação;
metadataTrad.dc.date.issued 2020-06-30;
metadataTrad.dc.description.sponsorship Nenhuma;
metadataTrad.dc.rights openAccess;
metadataTrad.dc.identifier.uri http://www.repositorio.jesuita.org.br/handle/UNISINOS/9378;
metadataTrad.dc.publisher.program Programa de Pós-Graduação em Engenharia Civil;


Files in this item

This item appears in the following Collection(s)

Show simple item record

Search

Advanced Search

Browse

My Account

Statistics